DENAIS® Latex Phase Compounded Rubber is a 95%-above natural rubber with outstanding performance in resistance to wet abrasion,tearing and cutting.
The unique Latex Liquid Phase Compounded Process gives our premium latex rubber extraordinary physical properties and outstanding performance, making DENAIS® Latex Rubber the top-quality wear-resistant rubber for wet abrasion services especially in mining slurry transportation by significantly lowering the costs for our customers.
DENAIS® Latex Rubber is a renewable resource and environmentally friendly, which uses NR latex to minimize impacts on environment and energy while maximizing safety, reliability and operational efficiency.
Superior slurry abrasion resistance
Good combination of mechanical strength
High coefficient of friction
High resilience and low modulus
Corrosion resistance to a wide range of chemicals
Excellent resistance to cutting and tearing
Environmentally friendly
Hot Vulcanized
Cold Bonded
High Temperature and Pressure Moulded
| Inspection Type | Test Standard | DENAIS® Latex Rubber |
| Tesile Strength (MPa) | ISO 37:2011 | >26 |
| Elongation (%) | ISO 37:2011 | >820 |
| Tear Strength (N/mm) | ASTM D624-00-2012 | >45 |
| Hardness (SHa) | ISO 48-2010 | 35±3 |
| Specific Gravity (g/cm²) | ISO 2781-2008 | 0.95~0.98 |
| Resilient Rate (%) | BS 903-Part A8:1990 | >80 |
| Wet Abrasion Index | 1.0~1.2 | |
| Operating Temperatures (continuous use) |
-40°C~70°C |
Slurry Pipe lining
Slurry Hoses
Slurry Pumps
Slurry Valve Liners
Hydro-cyclones Liners
Slurry Tank Linings
Screen Decks
Filter Presses
Standard sheet size: 9.25 m × 1.23 m nominal (approx. 30 ft × 4 ft)
Standard thickness range: 1.5 mm to 35.0 mm (approx. ¹⁄₁₆ to 1 ⅖ inch)
DENAIS® Latex Phase Compounded Rubber